Permeability properties of single jersey fabrics made of hollow yarns
Yükleniyor...
Dosyalar
Tarih
2017
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Taylor and Francis Ltd.
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this work effect of using hollow yarns on the permeability properties of the single jersey knitted fabrics were studied. Firstly yarns were produced by ring spinning machine using cotton, viscose and acrylic fibres in the mantle and water soluble polyvinyl alcohol (PVA) fibre in the core. Single jersey fabrics were knitted and PVA core was removed subsequently by washing process to create hollow yarn. Weight, air permeability and water transmission rate properties of fabrics were measured before and after washing and compared with reference fabrics. Due to the removal of PVA fibres from the yarn core after washing treatment, air permeability and water vapour transmission rate of the all kind of single jersey fabrics which were produced with hollow yarns increased as well as weight of the fabrics decreased which will cause more comfort during any exercise. It was also found that mantle fibre type and PVA ratio have significant effect on the fabric properties. © 2017 The Textile Institute.
Açıklama
Anahtar Kelimeler
air permeability, hollow yarn, Knitted fabric, PVA fibres, water vapour transmission rate, wetting, Air permeability, Fibers, Knit fabrics, Spinning (fibers), Textile fibers, Washing, Water vapor, Wetting, Wool, Yarn, Fabric properties, Knitted fabric, Permeability properties, Poly (vinyl alcohol) (PVA), Ring-spinning machines, Transmission rates, Washing treatment, Water transmission, Produced Water, Air Permeability, Cotton, Fabric, Permeability, Polyvinyl Alcohol, Washing, Yarn
Kaynak
Journal of the Textile Institute
WoS Q Değeri
Scopus Q Değeri
Q2
Cilt
108
Sayı
11