Joint performance of medium carbon steel-austenitic stainless steel double-sided TIG welds
Küçük Resim Yok
Tarih
2023
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Walter de Gruyter GmbH
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
AISI 1040 and AISI 304 steel plates of 10 mm were joined without pretreatment by double-sided TIG arc welding (DSAW). Joints were manufactured by using welding currents of 420, 440, and 460 A. The microstructural variations in the interface of the weld samples were defined by optical microscopy, scanning electron microscopy, energy dispersive spectroscopy and microhardness analysis. V-notch impact and tensile tests were done to detect the weld strength of the weld samples. In DSAW welding of different steels, a full penetration joint was achieved without opening the weld edge. The current intensity had a major effect on the symmetrical and hourglass shape in welds. Welding at 460 (A) showed acceptable joint quality. Tensile and impact energy quantities of welded joints had significant ratios. Fractures in the weld metal of the samples were ductile mode. © 2022 Walter de Gruyter GmbH, Berlin/Boston.
Açıklama
Anahtar Kelimeler
AISI 1040, AISI 304, DSAW, impact test, TIG, Austenitic stainless steel, Ductile fracture, Energy dispersive spectroscopy, Gas welding, Scanning electron microscopy, Tensile testing, AISI 1040, AISI 304, Aisi-304, Double sided, Double-sided TIG arc welding, Impact test, Joint performance, Medium-carbon steels, TIG, TIG arc welding, Welds
Kaynak
Materialpruefung/Materials Testing
WoS Q Değeri
Scopus Q Değeri
Q2
Cilt
65
Sayı
2