Evaluation of the Corrosion Resistance of Different Types of Orthodontic Fixed Retention Appliances: A Preliminary Laboratory Study
Yükleniyor...
Dosyalar
Tarih
2023
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Mdpi
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
(i) Objective: The present study aimed to compare the electrochemical corrosion resistance of six different types of fixed lingual retainer wires used as fixed retention appliances in an in vitro study. (ii) Methods: In the study, two different Ringer solutions, with pH 7 and pH 3.5, were used. Six groups were formed with five retainer wires in each group. In addition, 3-braided stainless steel, 6-braided stainless steel, Titanium Grade 1, Titanium Grade 5, Gold, and Dead Soft retainer wires were used. The corrosion current density (i(corr)), corrosion rate (CR), and polarization resistance (R-p) were determined from the Tafel polarization curves. (iii) Results: The corrosion current density of the Gold retainer group was statistically higher than the other retainer groups in both solutions (p < 0.05). The corrosion rate of the Dead Soft retainer group was statistically higher than the other retainer groups in both solutions (p < 0.05). The polarization resistance of the Titanium Grade 5 retainer group was statistically higher than the other retainer groups in both solutions (p < 0.05). As a result of Scanning Electron Microscope (SEM) images, pitting corrosion was not observed in the Titanium Grade 1, Titanium Grade 5 and Gold retainer groups, while pitting corrosion was observed in the other groups. (iv) Conclusion: From a corrosion perspective, although the study needs to be evaluated in vivo, the Titanium Grade 5 retainer group included is in this in vitro study may be more suitable for clinical use due to its high electrochemical corrosion resistance and the lack of pitting corrosion observed in the SEM images.
Açıklama
Anahtar Kelimeler
orthodontics, lingual retainer, electrochemical corrosion, pitting corrosion, current density, corrosion rate, polarization curve, Stainless-Steel, Artificial Saliva, In-Vitro, Ion Release, Behavior, Archwires, Fluoride, Wires, Brackets, Niti
Kaynak
Journal Of Functional Biomaterials
WoS Q Değeri
Q1
Scopus Q Değeri
Q2
Cilt
14
Sayı
2