Research on the fire endurance of the silica sand membrane
Yükleniyor...
Dosyalar
Tarih
2019
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Institute of Physics Publishing
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
In this study, the fire endurance, density, low-temperature deflection, penetration and ring-ball method tests of the membrane produced throughout the mixing of Bitumen, IPP (isotactic polypropylene), LDPE (Low-density polyethylene) calcite and silica sand at varying proportions were performed and the test results were compared with the membrane used today. In our study, TS 120 EN 1427, TS 118 EN 1426, TS EN 13501-1, KG-TL-029 testing methods were used. The density of the silica material we have obtained was measured at 1.3782 g/cm3, the endurance of the material was found out to be better, softening temperature was measured at 155 C, brittleness temperature at -7 C and the fire class was found out to be as E. © Published under licence by IOP Publishing Ltd.
Açıklama
22nd National Conference on Thermodynamics with International Participation, NACOT 2019 -- 23 May 2019 through 24 May 2019 -- -- 152413
Anahtar Kelimeler
C (programming language), Calcite, Fracture mechanics, Polypropylenes, Silica, Temperature, Fire endurances, Isotactic polypropylene, LDPE (low-density polyethylene), Low temperatures, Silica material, Softening temperature, Testing method, Silica sand