Optical and structural characteristics of electrodeposited Cd 1-xZnxS nanostructured thin films
Özet
The structural and optical characteristics of Cd1-xZnxS (CdZnS) thin films grown by the electrodeposition method were investigated in the present paper. The crystalline structure of the grown CdZnS thin film was determined as cubic wurtzite due to observed diffraction peaks associated with (111) and (220) planes. Atomic compositional ratios of the constituent elements were obtained using energy dispersive spectroscopy and doping concentration of the Zn was found as 5% (x ~ 0.05). Scanning electron microscopy image of the studied thin film indicated that grown film is nanostructured. Raman spectra of CdS and CdZnS thin films were measured and it was seen that observed longitudinal optical modes for CdZnS present a blue-shift. Temperature-dependent band gap energy characteristics of the thin films were studied performing transmission experiments in the 10–300 K temperature range. The analyses of the recorded transmittance spectra showed that direct band gap energy of the films decreases from 2.56 eV (10 K) to 2.51 eV (300 K) with the increase of temperature. The band gap energy vs. temperature dependency was studied applying well-known Varshni optical model and various optical parameters of the films were reported according to the results of the applied model. © 2021 Elsevier B.V.
Cilt
114Koleksiyonlar
İlgili Öğeler
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
-
Fiber optik kabloların kalite parametrelerinin belirlenmesi ve bu parametreler üzerine etki eden faktörlerin etki mekanizmalarının analizi
Polat, Mustafa Evren (Namık Kemal Üniversitesi, 2019)Haberleşme alanında çeşitli ortamlar ve amaçlar için farklı tiplerde fiber optik kablolar üretilmekte ve kullanılmaktadır. Üretilen fiber optik kablolar farklı çevresel ve mekanik şartlar altında farklı verim ve dayanım ... -
Temperature-dependent material characterization of CuZnSe2 thin films
Güllü, H. H.; Surucu, O.; Terlemezoğlu, Makbule; Işık, M.; Ercelebi, C.; Gasanly, Nizami Mamed; Parlak, Mehmet (Elsevier B.V., 2020)In the present work, CuZnSe2 (CZSe) thin films were co-deposited by magnetron sputtering of ZnSe and Cu targets. The structural analyses resulted in the stoichiometric elemental composition and polycrystalline nature without ... -
Structural, morphological and temperature-tuned bandgap characteristics of CuS nano-flake thin films
Işık, M.; Terlemezoğlu, Makbule; Gasanly, N.; Parlak, M. (Elsevier B.V., 2022)Copper sulfide (CuS) thin films were produced by radio-frequency (RF) magnetron sputtering method. Structural, morphological and optical characteristics of deposited CuS films were presented. X-ray diffraction pattern ...