Investigation on the Effect of Draw Ratio on Voltage Outputs of Polarised Isotactic Polypropylene Monofilaments
Özet
Piezoelectric isotactic polypropylene (iPP) monofilaments were prepared by drawing and poling on a laboratory scale melt extruder. Results showed that the filament properties are affected by the drawing ratio. As expected, an increase in draw ratio caused lower filament counts (thinner diameters), higher tensile strengths and higher crystallinities. To invetigate the effect of draw ratio on voltage output of produced samples, a rotational mass was applied onto the samples. Results showed that filaments subjected to a draw ratio of 2:1 had highest voltage output as compared to others. Produced filaments are found to be suitable for use in smart textiles.
Cilt
23Sayı
103Koleksiyonlar
İlgili Öğeler
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
-
The impact of RCA and fly ash on the mechanical and durability properties of polypropylene fibre-reinforced concrete exposed to freeze-thaw cycles and MgSO4 with ANN modeling
Bayraktar, Oğuzhan Yavuz; Eshtewı, S. Salem Taher; Benli, Ahmet; Kaplan, Gökhan; Toklu, Kenan; Günek, Furkan (Elsevier Ltd, 2021)An experimental study has been conducted to investigate the impact of recycled coarse aggregate (RCA) and fly ash (FA) on the transport, mechanical and durability properties of polypropylene fiber reinforced concretes. In ... -
Evaluation of fly ash and polypropylene in production of composite materials
Yıldız, T.; Argunhan, Z.; Haksever, Ayşen (2012)More than 10 million tons of fly ash produced in power plants and polypropylene wastes cause environmental pollution in Turkey. Not only the environmental problems they create, but also the fact that demand for raw material ... -
Surface appearance evaluation of some weft knitted fabric reinforced composites
Soyaslan, Devrim; Göktepe, Özer (Fiber Society, 2010)In this study, it was aimed to investigate the thermal effects of some weft knitted fabric reinforced polypropylene composites on the surface appearance. Polypropylene is the matrix phase and the aramid yarn and copper ...